FEATURES
|
TEST METHOD DIN
|
UNIT
|
VALUE
|
DENSITY
|
53479
|
gr/cm³
|
|
HEAT CONDUCTIVITY
|
52612
|
W/mk
|
0.31
|
VOLUMETRIC RESISTANCE
|
53482
|
OHM-cm
|
1015
|
SURFACE RESISTANCE
|
53482
|
OHM
|
1013
|
TENSILE RESISTANCE (YIELDING POINT)
|
53455
|
kg/cm²
|
700
|
TENSILE BREAKING STRETCHING
|
53455
|
%
|
50 - 75
|
HARDNESS Shore D
|
53505
|
|
80
|
TEMPERATURE OF USE
|
-
|
°C
|
50
|
FUSING POINT
|
Polarizer Microscope
|
°C
|
165 - 175
|
BENDING TEMPERATURE
|
53752
|
°C
|
125
|
3.5% BENDING TEMPERATURE
|
53452
|
Kg/cm²
|
700
|
WATER ABSORPTION ( 23 °C in water, 24 hours)
|
53495
|
%
|
0.2
|
IMPACT STRENGTH (Jagless )
|
53453
|
kJ/m2
|
Unbreakable
|
IMPACT STRENGTH (Jaggy )
|
53453
|
kJ/m2
|
??
|
SOFTENING TEMPERATURE (Vicat-B)
|
53460
|
°C
|
160
|
COEFFICIENT OF THERMAL EXPANSION (20 °C - 100 °C)
|
52328
|
I/K
|
1.1x10-4
|
COEFFICIENT OF FRICTION
|
-
|
-
|
0.25 - 0.4
|
DIELECTRIC STRENGTH (0.2 mm)
|
53481
|
KV/mm
|
55
|